Abstract：The microstrueture of laser melted Co base allog was studied.The results show that solid solubility was inereased and twin crystal was found in heat effect area. A lot of Fe,C solid solubility were deduees from results of Mssbauer spectrum.The fact that surface properies was improved rest in increasing crystal boundary.
收稿日期: 1997-04-25
引用本文:
甘仲惟 郑启光. 1Cr18Ni9Ti激光表面熔覆合金结构相的研究[J]. , 1997, 36(4): 0-0.
甘仲惟 郑启光. THE MICRO MECHANISM OF LASER ON SUBSTRATES WITH STAINLESS STEEL 1Cr 18 Ni 9Ti. , 1997, 36(4): 0-0.